HettaShield 125P Series
HettaShield is high-performance heat shrink tubing with excellent physical and mechanical properties where it excels in a wide variety of electrical applications, including automotive & marine wire harnesses, wire splices, breakouts, and connector-to-cable transitions.
​
​
HettaShield 125P Series Technical Highlights​
​
• 2:1 Shrink Ratio, 3:1 Shrink Ratio
• Low Longitudinal Shrinkage
• Flame Retardant Outer Jacket
• Seals against water, moisture, and other contaminants
• Continuous Operating temperature:-45°C- 125°C
• Shrink Temperature:125°C
​
​
​
​
​
HettaShield 125P-2X​
TECHNICAL DATA:
​
Property
​
Tensile strength (MPa)
Ultimate elongation (%)
Tensile strength after heat aged (MPa)
Ultimate elongation after heat aged (%)
Longitudinal chang (%)
Flammability
Voltage withstand
Dielectric strength (kV/mm)
Volume resistivity (Ω·cm)
Test method
​
ASTM D 2671
ASTM D 2671
1580C ×168h
1580C ×168h
ASTM D 2671
ASTM D 2671 C method
UL 224, 2500V, 60s
ASTM D 149
ASTM D 876
Standard Performance
​
≥10.4
≥200
≥7.3
≥100
-5% ~+5%
VW-1
No breakdown
≥15
≥1014
2:1 shrink ratio
Low longitudinal shrinkage Flame retardant
RoHS Compliant
Temperature: 125°C
Rating: 600V AC
Flame Rating: VW-1
Operating temperature: -55°C- 125°C
Shrink Temperature: ≥ 120°C
​
​
​
​
DIMENSIONS
​
Size
Inch
1/16
1/8
3/16
1/4
3/8
1/2
5/8
3/4-3/16
1
1 1/4
1 1/2
2
3
4
​
mm
​
1.5
3.0
4.5
6.0
9.0
12.0
15.0
18.0
25.0
30.0
40.0
50.0
60.0
70.0
80.0
90.0
100.0
Expanded
Internal
Diameter (mm)
2.0±0.2
3.5 ±0.2
5.0 ±0.2
6.5 ±0.2
9.5 ± 0.3
12.5 ±0.3
15.5 ±0.4
19.0 ±0.5
26.0 ±0. 5
31.5 ±1.0
41.5 ±1.0
≥50
≥60
≥70
≥80
≥90
≥100
After Recovery Internal
Diameter (mm)
≤0.85
≤1.50
≤2.30
≤3.00
≤4.50
≤6.00
≤7.50
≤9.00
≤12.5
≤15.0
≤20.0
≤25.0
≤31.0
≤36.0
≤41.0
≤46.0
≤51.0
​
≤0.85
≤1.50
≤2.30
≤3.00
≤4.50
≤6.00
≤7.50
≤9.00
≤12.5
≤15.0
≤20.0
≤25.0
≤31.0
≤36.0
≤41.0
≤46.0
≤51.0
Total Wall
Thickness
(mm)
Standard Package
Spool Length
M/Spool
​
200
200
100
100
100
100
100
100
50
50
50
25
25
25
25
25
25
HettaShield 125P-3X​
TECHNICAL DATA:
​
Property
​
Tensile strength (MPa)
Ultimate elongation (%)
Tensile strength after heat aged (MPa)
Ultimate elongation after heat aged (%)
Longitudinal chang (%)
Flammability
Voltage withstand
Dielectric strength (kV/mm)
Volume resistivity (Ω·cm)
Test method
​
ASTM D 2671
ASTM D 2671
1580C ×168h
1580C ×168h
ASTM D 2671
ASTM D 2671 C method
UL 224, 2500V, 60s
ASTM D 149
ASTM D 876
Standard Performance
​
≥10.4
≥200
≥7.3
≥100
-5% ~+5%
VW-1
No breakdown
≥15
≥1014
DIMENSIONS
​
Size
Inch
1/16
1/8
3/16
1/4
3/8
1/2
5/8
3/4-3/16
1
1 1/4
1 1/2
2
3
4
​
mm
​
1.5
3.0
4.5
6.0
9.0
12.0
15.0
18.0
24.0
30.0
39.0
50.0
60.0
70.0
80.0
90.0
100.0
Expanded
Internal
Diameter (mm)
1.6±0.1
3.2±0.1
4.7±0.1
6.2±0.1
9.3±0.2
12.3±0.2
15.3±0.4
18.3±0.2
24.4±0. 3
30.4±0.3
39.6±0.5
50.6±0.5
61.5±1.0
71.5±1.0
81.5±1.0
91.5±1.0
101.5±1.0
After Recovery Internal
Diameter (mm)
≤0.50
≤1.00
≤1.50
≤2.00
≤3.00
≤4.00
≤5.00
≤6.00
≤8.00
≤10.0
≤13.0
≤16.0
≤20.0
≤23.0
≤26.0
≤30.0
≤33.0
​
0.45±0.10
0.55±0.10
0.60±0.10
0.65±0.10
0.75±0.15
0.75±0.15
0.80±0.15
0.85±0.15
1.00±0.20
1.15±0.20
1.50±0.20
2.50±0.20
2.60±0.20
2.60±0.20
2.60±0.20
2.60±0.20
2.60±0.20
Total Wall
Thickness
(mm)
Standard Package
Spool Length
M/Spool
​
200
200
100
100
50
50
50
50
25
25
25
25
25
25
25
25
25